Two Step and Regression Re-aging Heat Treatment of Al-5.2%Zn-2.3%Mg Alloy Applied in Cigarette Making Machines

Wang, Hao and Zhan, Jianbo and Yu, Zhenhua and Yu, Jiang and Ji, Yafeng and Zhang, Ying and Wang, Tao and Yu, Yao and Li, Muyan and He, Danfeng and Zhang, Hongkui and Fu, Rongrong and Zan, Na and Ding, Wei and Li, Liwei and Cheng, Liang and Yue, Baoshan and Zheng, Han and Li, Zhiqiang and Gao, Li (2016) Two Step and Regression Re-aging Heat Treatment of Al-5.2%Zn-2.3%Mg Alloy Applied in Cigarette Making Machines. American Chemical Science Journal, 14 (4). pp. 1-10. ISSN 22490205

[thumbnail of Wang1442016ACSJ26486.pdf] Text
Wang1442016ACSJ26486.pdf - Published Version

Download (2MB)

Abstract

Deformation scheme and pre-heat treatment of Al-5.2%Zn-2.3%Mg aluminum alloy is chosen, homogenizing annealing at 415℃ for 1h, cooling to 200℃ in furnace at a cooling rate of less than 30℃/ h and then cooling to room temperature to make Al-5.2%Zn-2.3%Mg aluminum alloy annealed fully. Heat treatment tests of Al-5.2%Zn-2.3%Mg aluminum alloy mainly consisting of rolling and aging were conducted, and the optimum peak aging mechanism is 120℃/20 h. Through comparison of microstructure and mechanical properties with different deformation and aging mechanism, effect of deformation rates and aging mechanism on properties of Al-5.2%Zn-2.3%Mg aluminum alloy was analyzed, and optimum double-peak aging mechanism is 110℃/7h+170℃/16 h. Orthogonal experiments were carried out to analyze mechanical and electrical properties of tested materials before and after deformation, and effect of aging mechanism on Al-5.2%Zn-2.3%Mg Al alloy was analyzed, and the optimum regression aging mechanism is 120℃/20 h+170℃/40 min+120℃/20 h.

Item Type: Article
Subjects: Science Global Plos > Chemical Science
Depositing User: Unnamed user with email support@science.globalplos.com
Date Deposited: 24 May 2023 08:32
Last Modified: 20 Jan 2024 10:42
URI: http://ebooks.manu2sent.com/id/eprint/947

Actions (login required)

View Item
View Item